Comment by 3am

Would this actually be a pretty bad application of 3-d printing? I thought the metals were generally or exclusively done through sintering, and and for some reason (may be incorrect) it didn't do as well with tensile & deformation stress. Not to mention porosity. Seems like something a casted product would be better for.